Title: Submerged Fatigue Testing of Marine Energy Advanced Materials

Authors: Ariel F. Lusty, Paul Murdy, Julia A. Gionet-Gonzales

DOI: 10.33599/nasampe/s.24.0124

Abstract: Marine energy structures are typically made of advanced composite materials and are subjected to extreme ocean environments in service. In extreme ocean environments, seawater currents and waves load structures repeatedly, which cause two environmental conditions: water intrusion and mechanical fatigue. In prior research, the two environmental conditions were applied sequentially, where composite specimens were aged and then mechanically tested. To understand the combined effects of dynamic loading and water intrusion on composite materials, the present study involves the static and fatigue four-point bend testing of composite coupons in a water tank. The water tank was designed and built to fit either a 100 kN or a 250 kN load frame. Flexural strength value, cycles to failure, and failure mode results from submerged fatigue testing will be used to inform marine energy structure designs. The coupon-scale test method will be used to scale up to and inform methods for subsequent subcomponent testing and standards development. The benefits of designing marine energy structures to informed standards are decreased lifetime costs and increased reliability and energy production, ultimately leading to a sustainable and low-carbon energy system.

References: 1.Water Power Technologies Office: Multi-Year Program Plan. 2022: United States. 2.Augustine, C., et al., Renewable Electricity Futures Study. Volume 2: Renewable Electricity Generation and Storage Technologies. (Volume 2 of 4). 2012, National Renewable Energy Laboratory. 3.Hernandez-Sanchez, B.A., et al. Evaluation of composite materials for wave and current energy technologies. 2019. United States. 4.Meng, M., et al., Moisture effects on the bending fatigue of laminated composites. Composite structures, 2016. 154: p. 49-60. 5.Murdy, P., et al., Subcomponent Validation of Composite Joints for the Marine Energy Advanced Materials Project. 2023. 6.Jiang, Y., et al., Structural analysis of a fibre-reinforced composite blade for a 1 MW tidal turbine rotor under degradation of seawater. Journal of ocean engineering and marine energy, 2023. 9(3): p. 477-494. 7.Boresi, A.P., Schmidt, Richard J, Advanced Mechanics of Materials. Sixth ed. 2003, Hoboken, NJ: John Wiley & Sons, Inc. 8.Barbero, E., Introduction to Composite Materials Design. Second Edition ed. 2011, Boca Raton, FL: CRC Press. 9.Selvarathinam, A.S. and Y.J. Weitsman, A shear-lag analysis of transverse cracking and delamination in cross-ply carbon-fibre/epoxy composites under dry, saturated and immersed fatigue conditions. Composites Science and Technology, 1999. 59(14): p. 2115-2123. 10.Selvarathinam, A.S. and Y.J. Weitsman, Transverse cracking and delamination in cross-ply gr/ep composites under dry, saturated and immersed fatigue. International Journal of Fracture, 1998. 91(2): p. 103-116. 11.Cousins, D.S., et al., Recycling glass fiber thermoplastic composites from wind turbine blades. Journal of Cleaner Production, 2019. 209: p. 1252-1263. 12.Murray, R.E., et al., Manufacturing a 9-Meter Thermoplastic Composite Wind Turbine Blade: Preprint. 2017, National Renewable Energy Laboratory. 13.Sperling, L.H., Introduction to physical polymer science. 2006, Wiley: Hoboken, N.J. 14.Lerman, M.W., D.S. Cairns, and J.W. Nelson, Investigation of the Effect of In-Plane Fiber Waviness in Composite Materials through Multiple Scales of Testing and Finite Element Modeling. 2017: United States. 15.D7264/D7264M Standard Test Method for Flexural Properties of Polymer Matrix Composite Materials. 2015. 16.Bharath, A., et al. Open Water Blade Strain Measurements on a Vertical-Axis Tidal Turbine. 2023. United States: New York, NY: American Society of Mechanical Engineers (ASME). 17.Murray, R.E., et al. Toward the Instrumentation and Data Acquisition of a Tidal Turbine in Real Site Conditions. 2023. 16, 1255 DOI: 10.3390/en16031255. 18.International, A., Standard Test Method for Moisture Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite Materials. 2020, ASTM International: West Conshohocken, PA. 19.Gintert, L.A., Element and Subcomponent Testing, in Composites, D.B. Miracle and S.L. Donaldson, Editors. 2001, ASM International. p. 0. 20.Fernandes, R.L., M.F.S.F. de Moura, and R.D.F. Moreira, Effect of moisture on pure mode I and II fracture behaviour of composite bonded joints. International Journal of Adhesion and Adhesives, 2016. 68: p. 30-38. 21.Rocha, I.B.C.M., et al., Experimental/numerical study of anisotropic water diffusion in glass/epoxy composites. IOP Conference Series: Materials Science and Engineering, 2016. 139(1): p. 012044. 22.Pipes, R.B. and N.J. Pagano, Interlaminar Stresses in Composite Laminates Under Uniform Axial Extension. Journal of Composite Materials, 1970. 4(4): p. 538-548.

Conference: SAMPE 2024

Publication Date: 2024/05/20

SKU: TP24-0000000124

Pages: 16

Price: $32.00