Title: Effect of Humidity and Temperature on the Strength of Repaired Woven Fabric Composites

Authors: Evren Sonat, Mete Bakır, Sezer Ozerinc

DOI: 10.33599/nasampe/s.25.0221

Abstract: The durability of repaired CFRP components under environmental conditions such as high humidity and temperature is critical for reliable long-term operation. This study investigates the effects of temperature and moisture on the repair strength of prepreg and wet lay-up repairs performed on M21/AS4C carbon/epoxy fabric panels. A series of wet lay-up and prepreg steprepaired specimens produced according to standardized aerospace procedures were tested under uniaxial tension. For each case, dry specimens and hot-wet specimens immersed in water at 70°C for 14 days were considered. The experimental measurements on 3.8° scarf angle repairs showed that the strength recovery could be as high as 68% for the prepreg repairs and 59% for the wet lay-up repairs for unconditioned specimens. The moisture and humidity exposure did not have a significant impact on the strength of the prepreg-based repairs. Wet lay-up repaired specimens, on the other hand, showed a 30% reduction in strength upon exposure to humidity and temperature. The results show that prepreg repairs should be preferred over wet lay-up repairs for the long-term reliable operation of repaired components.

References: [1] J. Young, “Formula One motorsport – racing with materials,” Interdisciplinary Science Reviews, vol. 24, no. 1, pp. 58–63, Jan. 1999, doi: 10.1179/030801899678632. [2] J. Lowe, “11 - Aerospace applications,” in Design and Manufacture of Textile Composites, A. C. Long, Ed., in Woodhead Publishing Series in Textiles. , Woodhead Publishing, 2005, pp. 405–423. doi: 10.1533/9781845690823.405. [3] J. Zhang, G. Lin, U. Vaidya, and H. Wang, “Past, present and future prospective of global carbon fibre composite developments and applications,” Composites Part B: Engineering, vol. 250, p. 110463, Feb. 2023, doi: 10.1016/j.compositesb.2022.110463. [4] Y. Li, Y. Xiao, L. Yu, K. Ji, and D. Li, “A review on the tooling technologies for composites manufacturing of aerospace structures: materials, structures and processes,” Composites Part A: Applied Science and Manufacturing, vol. 154, p. 106762, Mar. 2022, doi: 10.1016/j.compositesa.2021.106762. [5] T. Wang, K. Huang, L. Guo, T. Zheng, and F. Zeng, “An automated vacuum infusion process for manufacturing high-quality fiber-reinforced composites,” Composite Structures, vol. 309, p. 116717, Apr. 2023, doi: 10.1016/j.compstruct.2023.116717. [6] M. R. Ricciardi et al., “A new cost-saving vacuum infusion process for fiber-reinforced composites: Pulsed infusion,” Journal of Composite Materials, vol. 48, no. 11, pp. 13651373, May 2014, doi: 10.1177/0021998313485998. [7] J. Summerscales and T. J. Searle, “Low-pressure (vacuum infusion) techniques for moulding large composite structures,” Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, vol. 219, no. 1, pp. 45–58, Jan. 2005, doi: 10.1243/146442005X10238. [8] A. Brasington, C. Sacco, J. Halbritter, R. Wehbe, and R. Harik, “Automated fiber placement: A review of history, current technologies, and future paths forward,” Composites Part C: Open Access, vol. 6, p. 100182, Oct. 2021, doi: 10.1016/j.jcomc.2021.100182. [9] J. W. Baur et al., “Mechanical properties of additively printed, UV cured, continuous fiber unidirectional composites for multifunctional applications,” Journal of Composite Materials, vol. 57, no. 4, pp. 865–882, Feb. 2023, doi: 10.1177/00219983221146264. [10] M. Sabaghi, Y. Cai, C. Mascle, and P. Baptiste, “Sustainability assessment of dismantling strategies for end-of-life aircraft recycling,” Resources, Conservation and Recycling, vol. 102, pp. 163–169, Sep. 2015, doi: 10.1016/j.resconrec.2015.08.005. [11] A. J. Timmis et al., “Environmental impact assessment of aviation emission reduction through the implementation of composite materials,” Int J Life Cycle Assess, vol. 20, no. 2, pp. 233–243, Feb. 2015, doi: 10.1007/s11367-014-0824-0. [12] I. D. Robertson et al., “Rapid energy-efficient manufacturing of polymers and composites via frontal polymerization,” Nature, vol. 557, no. 7704, pp. 223–227, May 2018, doi: 10.1038/s41586-018-0054-x. [13] M. Ziaee, J. W. Johnson, and M. Yourdkhani, “3D Printing of Short-Carbon-FiberReinforced Thermoset Polymer Composites via Frontal Polymerization,” ACS Appl. Mater. Interfaces, vol. 14, no. 14, pp. 16694–16702, Apr. 2022, doi: 10.1021/acsami.2c02076. [14] N. M. Larson, J. Mueller, A. Chortos, Z. S. Davidson, D. R. Clarke, and J. A. Lewis, “Rotational multimaterial printing of filaments with subvoxel control,” Nature, vol. 613, no. 7945, pp. 682–688, Jan. 2023, doi: 10.1038/s41586-022-05490-7. [15] H. Li and K. Englund, “Recycling of carbon fiber-reinforced thermoplastic composite wastes from the aerospace industry,” Journal of Composite Materials, vol. 51, no. 9, pp. 1265–1273, Apr. 2017, doi: 10.1177/0021998316671796. [16] R. Bernatas, S. Dagreou, A. Despax-Ferreres, and A. Barasinski, “Recycling of fiber reinforced composites with a focus on thermoplastic composites,” Cleaner Engineering and Technology, vol. 5, p. 100272, Dec. 2021, doi: 10.1016/j.clet.2021.100272. [17] G. Schinner, J. Brandt, and H. Richter, “Recycling Carbon-Fiber-Reinforced Thermoplastic Composites,” Journal of Thermoplastic Composite Materials, vol. 9, no. 3, pp. 239–245, Jul. 1996, doi: 10.1177/089270579600900302. [18] M. Rani, P. Choudhary, V. Krishnan, and S. Zafar, “A review on recycling and reuse methods for carbon fiber/glass fiber composites waste from wind turbine blades,” Composites Part B: Engineering, vol. 215, p. 108768, Jun. 2021, doi: 10.1016/j.compositesb.2021.108768. [19] S. Maiti, M. R. Islam, M. A. Uddin, S. Afroj, S. J. Eichhorn, and N. Karim, “Sustainable Fiber-Reinforced Composites: A Review,” Advanced Sustainable Systems, vol. 6, no. 11, p. 2200258, 2022, doi: 10.1002/adsu.202200258. [20] E. Pakdel, S. Kashi, R. Varley, and X. Wang, “Recent progress in recycling carbon fibre reinforced composites and dry carbon fibre wastes,” Resources, Conservation and Recycling, vol. 166, p. 105340, Mar. 2021, doi: 10.1016/j.resconrec.2020.105340. [21] W. Guo, S. Bai, Y. Ye, and L. Zhu, “Recycling carbon fiber-reinforced polymers by pyrolysis and reused to prepare short-cut fiber C/C composite,” Journal of Reinforced Plastics and Composites, vol. 38, no. 7, pp. 340–348, Apr. 2019, doi: 10.1177/0731684418822144. [22] B. Rijo, A. P. S. Dias, and J. P. S. Carvalho, “Recovery of carbon fibers from aviation epoxy composites by acid solvolysis,” Sustainable Materials and Technologies, vol. 35, p. e00545, Apr. 2023, doi: 10.1016/j.susmat.2022.e00545. [23] C. Morin, A. Loppinet-Serani, F. Cansell, and C. Aymonier, “Near- and supercritical solvolysis of carbon fibre reinforced polymers (CFRPs) for recycling carbon fibers as a valuable resource: State of the art,” The Journal of Supercritical Fluids, vol. 66, pp. 232240, Jun. 2012, doi: 10.1016/j.supflu.2012.02.001. [24] M. Prinçaud, C. Aymonier, A. Loppinet-Serani, N. Perry, and G. Sonnemann, “Environmental Feasibility of the Recycling of Carbon Fibers from CFRPs by Solvolysis Using Supercritical Water,” ACS Sustainable Chem. Eng., vol. 2, no. 6, pp. 1498–1502, Jun. 2014, doi: 10.1021/sc500174m. [25] J. D. Feist, D. C. Lee, and Y. Xia, “A versatile approach for the synthesis of degradable polymers via controlled ring-opening metathesis copolymerization,” Nat. Chem., vol. 14, no. 1, pp. 53–58, Jan. 2022, doi: 10.1038/s41557-021-00810-2. [26] J. D. Feist and Y. Xia, “Enol Ethers Are Effective Monomers for Ring-Opening Metathesis Polymerization: Synthesis of Degradable and Depolymerizable Poly(2,3dihydrofuran),” J. Am. Chem. Soc., vol. 142, no. 3, pp. 1186–1189, Jan. 2020, doi: 10.1021/jacs.9b11834. [27] P. Shieh et al., “Cleavable comonomers enable degradable, recyclable thermoset plastics,” Nature, vol. 583, no. 7817, pp. 542–547, Jul. 2020, doi: 10.1038/s41586-020-24952. [28] C. Lefay and Y. Guillaneuf, “Recyclable/degradable materials via the insertion of labile/cleavable bonds using a comonomer approach,” Progress in Polymer Science, vol. 147, p. 101764, Dec. 2023, doi: 10.1016/j.progpolymsci.2023.101764. [29] S. Vyas et al., “Through-thickness frontal polymerization: Process development and optimization,” Composites Part A: Applied Science and Manufacturing, vol. 180, p. 108084, May 2024, doi: 10.1016/j.compositesa.2024.108084. [30] E. M. Lloyd et al., “Efficient Manufacture, Deconstruction, and Upcycling of HighPerformance Thermosets and Composites,” ACS Appl. Eng. Mater., vol. 1, no. 1, pp. 477485, Jan. 2023, doi: 10.1021/acsaenm.2c00115. [31] O. Davydovich et al., “Frontal Polymerization of Dihydrofuran Comonomer Facilitates Thermoset Deconstruction,” Chem. Mater., vol. 34, no. 19, pp. 8790–8797, Oct. 2022, doi: 10.1021/acs.chemmater.2c02045. [32] Z. Dai, F. Shi, B. Zhang, M. Li, and Z. Zhang, “Effect of sizing on carbon fiber surface properties and fibers/epoxy interfacial adhesion,” Applied Surface Science, vol. 257, no. 15, pp. 6980–6985, May 2011, doi: 10.1016/j.apsusc.2011.03.047. [33] Z. Dai, B. Zhang, F. Shi, M. Li, Z. Zhang, and Y. Gu, “Effect of heat treatment on carbon fiber surface properties and fibers/epoxy interfacial adhesion,” Applied Surface Science, vol. 257, no. 20, pp. 8457–8461, Aug. 2011, doi: 10.1016/j.apsusc.2011.04.129. [34] S. Qiu, C. A. Fuentes, D. Zhang, A. W. Van Vuure, and D. Seveno, “Wettability of a Single Carbon Fiber,” Langmuir, vol. 32, no. 38, pp. 9697–9705, Sep. 2016, doi: 10.1021/acs.langmuir.6b02072. [35] L. T. Drzal, M. Madhukar, and M. C. Waterbury, “Adhesion to carbon fiber surfaces: Surface chemical and energetic effects,” Composite Structures, vol. 27, no. 1, pp. 65–71, Jan. 1994, doi: 10.1016/0263-8223(94)90068-X. [36] D. J. Eyckens et al., “Carbon fibre surface chemistry and its role in fibre-to-matrix adhesion,” Journal of Materials Chemistry A, vol. 9, no. 47, pp. 26528–26572, 2021, doi: 10.1039/D1TA07151C. [37] F. Vautard, S. Ozcan, F. Paulauskas, J. E. Spruiell, H. Meyer, and M. J. Lance, “Influence of the carbon fiber surface microstructure on the surface chemistry generated by a thermo-chemical surface treatment,” Applied Surface Science, vol. 261, pp. 473–480, Nov. 2012, doi: 10.1016/j.apsusc.2012.08.038.

Conference: SAMPE 2025

Publication Date: 2025/05/19

SKU: TP25-0000000221

Pages: 14

Price: $28.00